| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 24小时吸水率 | ASTM D-570 | 1.5 | % | ||
| 物理性能 | 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | 9 | mg/1000rev | |
| 比重 | ASTM D-792 | 1.22 | ||||
| 泰伯磨耗量 | H 18轮 | ASTM D-1044 | 116 | mg/1000rev | ||
| 熔体流动速率 | ASTM D-1238 | 10 | g/10min | |||
| 机械性能 | 初耐撕裂性能 | ASTM D-1004 | 123 | kn/m | ||
| 断裂伸长 | ASTM D-648 | 375 | % | |||
| 拉伸力 | 5%伸长 | ASTM D-638 | 6.0 | MPa | ||
| 10%伸长 | ASTM D-638 | 10.5 | MPa | |||
| 硬度计硬度 | ASTM D-2240 | 55 | ||||
| 断裂拉伸力 | ASTM D-638 | 31 | MPa | |||
| 揉曲模量 | 23℃ | ASTM D-790 | 193 | MPa | ||
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 不破裂 | J/m | ||
| 热性能 | 熔点 | ASTM D-3418 | 215 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 196 | ℃ | |||
| 热畸变温度 | @0.18Mpa | ASTM D-648 | 51 | ℃ | ||
| 热畸变温度 | @0.5Mpa | ASTM D-648 | 111 | ℃ | ||
| 其它性能 | 耐揉曲切口增长性能 | ASTM D-1052 | >8×105 | |||